Resin of LTPZE-2000 serials is reinforced composite for special materials of electric appliance based on high linear PPS. For their good electricity characteristics and thermal resistance, they are suitable to wave-soldering with many jointbar, mold in varied electronic component and supersonic bonding parts and integrated circuit package.
Mechanics of machinery data for LTP ZE-2000 serials materials
|
Item |
Unit |
Test method |
ZE-2100 |
ZE-2125 |
ZE-2150 |
ZE-2180 |
|
Tensile strength |
Mpa |
GB1040 |
100 |
125 |
150 |
180 |
|
Rate of elongation |
% |
GB/T1040 |
1.2 |
1.2 |
1.0 |
1.0 |
|
Flexural strength |
Mpa |
GB1042 |
120 |
150 |
180 |
200 |
|
Impact strength
(notched) |
KJ/m2 |
GB/T1043 |
|
|
|
|
|
Temperature of
thermal
deformation
|
℃ |
GB1634 |
|
|
|
|
|
Flame retard properties |
|
UL94 |
5V-V2 |
|
Dielectric strength |
KV/mm |
GB1408 |
20-35 |
|
Dielectric constant
（25℃） |
1KHz |
GB/T1409 |
2.2-3.0 |
|
1KHz |
2.2-3.0 |
|
Loss factor
（25℃） |
1KHz |
GB/T1409 |
0.001-0.003 |
|
1KHz |
0.001-0.003 |
|
Arc tight properties |
S |
D495 |
110-180 |
|
volume resistivity |
.cm |
GB/T1040 |
3×1014-8×1016 |
|
sheet resistance |
|
TB/T1040 |
5×1015-3×1017 |
|
Arc index |
V |
UL746A |
120-250 |
|
Mold shrinkage rate
Flow
directional
Vertical direcational
|
m/m |
80×80×3.0 |
0.002-0.004 |
|
0.003-0.006 |
|
Density |
Kg/m3 |
GB1033 |
1450-1800 |
|
Water absorption |
|
GB1034 |
0.2-0.4 |
|
color |
|
Visual method |
Varied Colour |